Calcium and phosphorus levels in saliva are influenced by genetic polymorphisms in estrogen receptor alpha and microrna17

Abstract Homeostasis between salivary calcium and phosphorus is important for maintaining oral health. The aim of this study was to evaluate if polymorphisms in ESR1 (Estrogen Receptor Alpha), ESR2 (Estrogen Receptor Beta) and miRNA17 (microRNA17) are associated with calcium and phosphorus levels in saliva. Saliva from 276 12-year-old children were collected by masticatory stimulation and calcium and phosphorus levels were determined by Mass Spectrometry. Genomic DNA was extracted from remaining saliva and genetic polymorphisms in ESR1 (rs12154178, rs1884051, rs9340799 and rs2234693), in ESR2 (rs4986938 and rs1256049) and in miRNA17 (rs4284505) were genotyped using TaqMan chemistry and a real-time PCR equipment. Statistical differences in genotype and allele distributions between 'low' and 'high' calcium and phosphorus levels were determined using chi-square or Fisher´s exact tests. The analysis was also adjusted by sex (alpha of 5%). ESR1 rs9340799 had the less common genotype associated with higher calcium levels (p=0.03). The less common allele of ESR1 rs1884051 was associated with lower phosphorus levels (p=0.005) and there was an excess of heterozygotes for miRNA17 rs4284505 among individuals with lower calcium levels (p=0.002), both adjusted by sex. This study provides evidence that genetic polymorphisms in ESR1 and miRNA17 are involved in determining salivary calcium and phosphorus levels.

Resumo A homeostasia entre cálcio e fósforo salivares é importante para a manutenção da saúde bucal. O objetivo deste estudo foi avaliar se polimorfismos genéticos no receptor de estrógeno alfa (ESR1), receptor de estrógeno beta (ESR2) e no microRNA17 (microRNA17) estão associados com os níveis salivares de cálcio e fósforo. Saliva de 276 crianças com 12 anos de idade foi coletada com estímulo mastigatório e os níveis de cálcio e fósforo foram determinados por Espectrofotometria de Massa. O DNA genômico foi extraído da saliva remanescente e os polimorfismos genéticos em ESR1 (rs12154178, rs1884051, rs9340799 e rs2234693), em ESR2 (rs4986938 e rs1256049) e no miRNA17 (rs4284505) foram genotipados pela reação em cadeia da polimerase em tempo real utilizando sondas TaqMan. As diferenças estatísticas nas distribuições alélicas e genotípicas entre "baixo" e "alto" níveis de cálcio e fósforo foram determinadas usando os testes qui-quadrado e teste exato de Fisher. As análises foram ajustadas por sexo (alfa de 5%). O polimorfismo rs9340799 em ESR1 foi o genótipo menos comum associado com altos níveis de cálcio (p=0,03). O alelo menos comum em ESR1 rs1884051 foi associado com baixos níveis de fósforo (p=0,005) e houve um excesso de heterozigotos para miRNA17 rs4284505 entre os indivíduos com baixos níveis de cálcio salivar (p=0,002), ambos ajustados pelo sexo. Este estudo fornece evidências de que polimorfismos genéticos em ESR1 e miRNA17 estão envolvidos na determinação dos níveis de cálcio e fósforo salivares.

Tissue response after subcutaneous implantation of different glass ionomer-based cements

Abstract The aim of this study was to evaluate the subcutaneous connective tissue response of isogenic mice after implantation of different glass ionomer-based cements (EQUIA® Forte Fil, EQUIA® Fil and Ketac™ Universal Aplicap™). Eighty-seven isogenic BALB/c mice were allocated in 12 groups, 9 were considered as experimental groups (Ketac, E. Fil and E. Forte at 7, 21 and 63 days) and 3 controls (empty polyethylene tubes at 7, 21 and 63 days). After the experimental periods, the subcutaneous connective tissue surrounding the implanted material was removed and subjected to histotechnical processing and staining with hematoxylin and eosin. A histopathological description of the tissue reaction surrounding each material and a semi-quantitative analysis of collagen fiber formation and inflammatory infiltrate were performed. Additionally, the thickness of the granulomatous tissue in contact with each material was measured. Data were analyzed statistically (α=0.05) by the Kruskal-Wallis test, followed by Dunn post-test. Initially, the collagen fiber formation was not different among all the tested materials (p>0.05) but was different at 21 days with the control group presenting the most advanced stage of collagen fiber formation. At 63 days, EQUIA® Forte Fil group showed the most advanced stage of collagen fiber formation, compared to EQUIA® Fil group (p<0.05). The inflammatory infiltrate was not different among the tested materials in any experimental period (p>0.05). The thickness of the granulomatous tissue was greater in the E. Forte group, compared to control in all periods. All glass ionomer-based cements showed tissue compatibility, according to the evaluated parameters.

Resumo O objetivo deste estudo foi avaliar a resposta subcutânea do tecido conjuntivo de camundongos isogênicos após o implante de diferentes cimentos à base de ionômero de vidro (EQUIA® Forte Fil, EQUIA® Fil e Ketac ™ Universal Aplicap ™). Oitenta e sete camundongos isogênicos BALB/c foram alocados em 12 grupos, 9 como grupos experimentais (Ketac, E. Fil e E. Forte aos 7, 21 e 63 dias) e 3 controles (tubos de polietileno vazios aos 7, 21 e 63 dias). Após os períodos experimentais, o tecido conjuntivo subcutâneo ao redor do material implantado foi removido e submetido ao processamento histotécnico e coloração com hematoxilina e eosina. Uma descrição histopatológica da reação tecidual envolvendo cada material e uma análise semi-quantitativa da fibrose e infiltrado inflamatório foram realizadas. Além disso, foi realizada a mensuração da espessura do tecido granulomatoso em contato com cada material. Os dados foram analisados estatisticamente (α=0,05) pelo teste de Kruskal-Wallis, seguido do pós-teste de Dunn. Inicialmente, a fibrose não foi diferente entre todos os materiais testados (p>0,05), mas foi diferente aos 21 dias, com o grupo controle apresentando o estágio mais avançado de fibrose. Aos 63 dias, o grupo EQUIA® Forte Fil apresentou o estágio mais avançado de fibrose, comparado ao grupo EQUIA® Fil (p<0,05). O infiltrado inflamatório não foi diferente entre os materiais testados em nenhum período experimental (p>0,05). A espessura do tecido granulomatoso foi maior no grupo E. Forte, comparado ao controle em todos os períodos. Todos os cimentos à base de ionômero de vidro apresentaram compatibilidade tecidual, de acordo com os parâmetros avaliados.

Adhesion and Initial Colonization of Streptococcus mutans is Influenced by Time and Composition of Different Composites / La Adhesión y la Colonización Inicial de Streptococcus mutans están Asociadas al Tiempo y la Composición de Diferentes Compuestos

ABSTRACT: The aim of this study was to evaluate the adhesion and initial colonization of S. mutans on the surface of novel composite resins during three experimental periods. Biofilms were formed on specimens of Enamel Plus HRI (Hri), FiltekTM Silorane (Si), Tetric EvoCeram® Bulk Fill (Te), KaloreTM (K), and FiltekTM Z250 (Z) (n=4/experimental period). After 4, 8 and 24 hours, the specimens were assessed for bacterial colony forming unit (CFU/mm2) levels and scanned by electron microscopy. All material surfaces showed a similar susceptibility to bacterial adhesion at 4 hours (p>0.05). The amount of microorganisms in the formed biofilms increased at 8 hours for all groups (p<0.05) and decreased at 24 hours only for Te and Z groups (p<0.05). After 24 h, the K group showed higher microorganism counts compared to the other groups. All composite resins evaluated were susceptible to adhesion by streptococci. However, bacteria attachment was not sufficient to maintain S. mutans colonization on Tetric EvoCeram® Bulk Fill and FiltekTM Z250 composites. Composite K presented the highest mean values for bacterial adhesion. Also, it was observed that the composition of resins could interfere with colonization mechanisms.

RESUMEN: El objetivo de este estudio fue evaluar la adhesión y la colonización inicial de S. mutans en la superficie de nuevas resinas compuestas durante tres períodos experimentales. Las biopelículas se formaron en muestras de Enamel Plus HRI (Hri), FiltekTM Silorane (Si), Tetric EvoCeram® Bulk Fill (Te), KaloreTM (K) y FiltekTM Z250 (Z) (n = 4 / período experimental). Después de 4, 8 y 24 horas, las muestras se evaluaron para determinar los niveles de la unidad formadora de colonias bacterianas (UFC / mm2) y se escanearon por microscopía electrónica. Todas las superficies del material mostraron una susceptibilidad similar a la adhesión bacteriana a las 4 horas (p> 0,05). La cantidad de microorganismos en las biopelículas formadas aumentó a las 8 horas para todos los grupos (p <0,05) y disminuyó a las 24 horas solo para los grupos Te y Z (p <0,05). Después de 24 horas, el grupo K mostró mayores recuentos de microorganismos en comparación con los otros grupos. Todas las resinas compuestas evaluadas fueron susceptibles a la adhesión por estreptococos. Sin embargo, la unión de bacterias no fue suficiente para mantener la colonización de S. mutans en los compuestos Tetric EvoCeram® Bulk Fill y FiltekTM Z250. El compuesto K presentó los valores medios más altos para la adhesión bacteriana. Además, se observó que la composición de las resinas podría interferir con los mecanismos de colonización.

Glass ionomer cements can be used for bonding orthodontic brackets after cancer radiation treatment?

Abstract Patients undergoing radiotherapy treatment present more susceptibility to dental caries and the use of an orthodontic device increases this risk factor due to biofilm accumulation around the brackets. The objective of this study was to evaluate the shear bond strength to irradiated permanent teeth of orthodontic brackets bonded with conventional glass ionomer cement and resin-modified glass ionomer cement due to the fluoride release capacity of these materials. Ninety prepared human premolars were divided into 6 groups (n=15), according to the bonding material and use or not of radiation: CR: Transbond XT composite resin; RMGIC: Fuji Ortho LC conventional glass ionomer cement; GIC: Ketac Cem Easymix resin-modified glass ionomer cement. The groups were irradiated (I) or non-irradiated (NI) prior to bracket bonding. The specimens were subjected to a fractioned radiation dose of 2 Gy over 5 consecutive days for 6 weeks. After the radiotherapy, the brackets were bonded on the specimens with Transbond XT, Fuji Ortho LC and Ketac Cem Easymix. After 24 h, the specimens were subjected to shear bond strength test. The image of enamel surface (classified by Adhesive Remnant Index - ARI) was also evaluated and its frequency was checked among groups/subgroups. The shear bond strength variable was evaluated with ANOVA and Tukey's post-hoc test. GIC group showed the lowest adhesion values among the groups (p<0.05). There was no statistically significant difference among non-irradiated and irradiated groups (p>0.05). As for the ARI, the CR-I group showed the highest material retention on enamel surface among the irradiated groups. RMGIC group showed the highest values for shear bond strength and presented ARI acceptable for clinical practices.

Resumo Pacientes submetidos a tratamento radioterápico apresentam maior suscetibilidade à cárie dentária e o uso de aparelho aumenta esse fator de risco devido ao acúmulo de biofilme dental ao redor dos bráquetes. Assim, o objetivo deste estudo foi avaliar a resistência ao cisalhamento de bráquetes ortodônticos colados com cimento de ionômero de vidro convencional (CIV) e o modificado por resina (CIVMR), devido à capacidade de liberação de flúor desse material em dentes permanentes irradiados. Noventa pré-molares humanos foram divididos em 6 grupos (n=15), de acordo com o materila de colagem e com o uso ou não de radiação: RC: Transbond XT; CIVMR: Fuji Ortho LC; RMGIC: Ketac Cem Easymix. Os grupos for irradiados (I) ou não-irradiados (NI) previamente à colagem dos bráquetes. Os espécimes foram submetidos a doses fracionadas de radiação de 2 Gy/dia, durante 5 dias consecutivos, por 6 semanas. Depois da termociclagem e radioterapia, os bráquetes foram colados sobre os espécimes com Transbond XT, Fuji Ortho LC e Ketac Cem Easymix. Depois de 24 h, os espécimes foram sumetidos ao teste de resistência ao cisalhamento. A imagem da superfície do esmalte (classificado pelo Índice de Remanescente Adesivo-IRA) também foi avaliada. O IRA foi distribuido em tabelas de contingência e analisado quanto à frequência entre grupos/subgrupos. O teste de resistência ao cisalhamento foi avaliado por ANOVA e pós-teste de Tukey. CIVMR apresentou os menores valores de adesão entre os grupos (p<0,05). Entre os grupos irradiados e não-irradiados não houve diferença estatística significante (p>0,05). Quanto ao IRA, RC-I apresentou maior retenção de compósito na superfície do esmalte do que os demais subgrupos. CIVMR pode ser utilizado para colagem de bráquetes metálico e apresentou IRA aceitável para práticas clínicas.